Description
405nm:
Light-curing, biocompatible, for 3D printing. For the generative production of basic parts of removable orthodontic appliances, drilling and X-ray templates. Removal of non-polymerised residues in a two-stage process with isopropanol in an ultrasonic cleaning device. Light polymerisation units with LED lights or xenon flash light under inert gas atmosphere are recommended for post-curing. Subsequent fixing of orthodontic wire elements and auxiliary parts with Freeform fixgel modelling resin. Medical device Class IIa.
- Very high construction precision and stability;
- Good polishability;
- MMA-free, neutral in odour and taste;
- Fracture resistance, elasticity and moisture influence in accordance with orthodontic standards;
- Validated procedure for sterilisation in autoclaves.
- Flexural strength > 75 MPa; modulus of elasticity > 1650 MPa; final hardness > 82 Shore D; water absorption < 32 µg/mm³; solubility < 5 µg/mm³.
For DLP printers with a wavelength of 405 nm.
clear transparent
1000 g
385nm:
Light-curing, biocompatible, for 3D printing. For the generative production of basic parts of removable orthodontic appliances, drilling and X-ray templates. Removal of non-polymerised residues in a two-stage process with isopropanol in an ultrasonic cleaning device. Light polymerisation units with LED lights or xenon flash light under inert gas atmosphere are recommended for post-curing. Subsequent fixing of orthodontic wire elements and auxiliary parts with Freeform fixgel modelling resin. Medical device Class IIa.
- Very high construction precision and stability;
- Good polishability;
- MMA-free, neutral in odour and taste;
- Fracture resistance, elasticity and moisture influence in accordance with orthodontic standards;
- Validated procedure for sterilisation in autoclaves.
- Flexural strength > 75 MPa; modulus of elasticity > 1650 MPa; final hardness > 82 Shore D; water absorption < 32 µg/mm³; solubility < 5 µg/mm³.
For DLP printers with a wavelength of 385 nm.
clear transparent
1000 g